关于我们
Grade树脂种类
|
物理性质
| 比重 | ASTM D792 | Natural 或代表 color | - | 1.1 |
| 熔融指数 | ASTM D1238 | 220℃, 10kg | g/10min | 13 |
| 成型收缩率(MD) | ASTM D955 | Flow at 3.2mm(MD) | % | 0.29~0.36 |
| 成型收缩率(TD) | ASTM D955 | X-Flow at 3.2mm(TD) | % | 0.31~0.38 |
机械性质
| 拉伸强度(at yield) | ASTM D638 | 5mm/min | kgf/cm2 | 520 |
| 伸长率(at break) | ASTM D638 | 5mm/min | % | 25 |
| 拉伸模量 | ASTM D638 | 5mm/min | kgf/cm2 | 25000 |
| 断裂强度(at break) | ASTM D638 | 5mm/min | kgf/cm2 | 350 |
| 弯曲强度 | ASTM D790 | 2.8mm/min | kgf/cm2 | 750 |
| 弯曲模量 | ASTM D790 | 2.8mm/min | kgf/cm2 | 26000 |
| Izod冲击强度(notched) | ASTM D256 | 1/4 inch at 23°C | kgf·cm/cm | 10 |
| Izod冲击强度(notched) | ASTM D256 | 1/8 inch at 23°C | kgf·cm/cm | 11 |
| 硬度 | ASTM D785 | R-Scale | - | 113 |
| 铅笔硬度 | JIS K 5401 | 500g | - | H |
热学特性
| 热变形温度 | ASTM D648 | 18.56kgf/cm2, 6.4mm | °C | 92 |
| 热变形温度 | ASTM D648 | 4.6kgf/cm2, 6.4mm | °C | 98 |
| 维卡软化温度 | ISO R 306 | B/50 | °C | 100 |
阻燃
| 阻燃度 | UL94 | HB | mm | 1.5, 3.0 |